Influence of heat treatment on microhardness and microstructure of the joining interface for Ti-24Al-15Nb-1.5Mo/TC11
发布时间：2024-08-09
点击次数：
- 所属单位：
- 冶金工程学院
- 发表刊物：
- Advance Materials Research
- 关键字：
- 中文关键字：Ti-24Al-15Nb-1.5Mo/TC11；热处理；显微硬度；显微组织，英文关键字：Ti-24Al-15Nb-1.5Mo/TC11；heat treatment；microhardne
- 摘要：
- The microhardness and microstructure of Ti-24Al-15Nb-1.5Mo/TC11 dual alloy joining interface processed by different heat treatment regimes were investigated. The results show that the microhardness of the weld zone and Ti-24Al-15Nb-1.5Mo alloy side of the dual alloy processed by gradient heat treatment are higher than that of the specimen processed by balance heat treatment. Moreover, the microstructure differences between the specimens processed by gradient heat treatment and balance heat treatment are very obvious, particularly in the interface between the TC11 alloy and the weld zone. While the joining interface is processed by gradient heat treatment, the microstructure change homogeneously, and the demarcation lines are ambiguous. However, for the joining interface processed by balance heat treatment, the demarcation lines are very obvious, and the microstructure of the TC11 alloy side is bi-morphic, the lath is short and coarse. Therefore, the interface integrity of the dual alloy processed by gradient heat treatment is better, which is an adoptable method to improve the properties of the dissimilar alloy joining interface.
- 备注：
- EI索引号: 20142717904460（刘莹莹）
- 合写作者：
- XinLin,WenxinZhang,YuanboZhang
- 第一作者：
- 刘莹莹
- 论文类型：
- 期刊论文
- 卷号：
- 卷：941-944
- 期号：
- 期：
- 页面范围：
- 页：2030-2034
- 是否译文：
- 否
- 发表时间：
- 2014-06-01