Study on the bubble behavior and anodic overvoltage of NiFe2O4 ceramic based inert anodes
发布时间：2024-08-09
点击次数：
- 所属单位：
- 冶金工程学院
- 发表刊物：
- Light Metals 2015 (EI会议)
- 关键字：
- 中文关键字：NiFe2O4陶瓷; 惰性阳极; 气泡行为; 阳极过电压;断电流法，英文关键字：NiFe2O4 Ceramic; Inert Anodes; Bubble behavior; An
- 摘要：
- NiFe2O4 ceramic based inert anodes were fabricated by a two-step cold-pressing sintering process. The bubble behavior of NiFe2O4 ceramic based inert anodes was investigated in a two-compartment see-through quartz cell. Anodic overvoltage and potential decay curves on the inert anodes were measured by using the steady state and current interruption technique. The results show that the electrolytic gas evolution for NiFe2O4 inert anodes, including bubble nucleation, growth, coalescence, growth again, migration and escaping, lasts for 79s and the escaping bubble size is about of Φ4mm×2mm. While gas evolution lasts for 102s of carbon anodes with larger releasing bubbles. When current densities are 0.6, 0.8, 1.0 and 1.2A/cm2, the anodic overvoltages of NiFe2O4 anodes are 0.189V, 0.270V, 0.309V and 0.359V, respectively. After adding small amount of MnO2, V2O5, and TiO2, a minor reduction in anodic overvoltage of NiFe2O4 anodes can be obtained.
- 备注：
- EI检索
- 合写作者：
- 刘宜汉,姚广春
- 第一作者：
- 胡平,方钊,王斌,杜金晶
- 论文类型：
- 期刊论文
- 卷号：
- 卷：
- 期号：
- 期：2015-January
- 页面范围：
- 页：1193-1197
- 是否译文：
- 否
- 发表时间：
- 2015-01-01