所属单位：冶金工程学院

发表刊物：Int. Journal of Refractory Metals and Hard Materials（SCI）

关键字：中文关键字：TZM合金；掺镧；力学性能；韧脆转变温度，英文关键字：TZM alloy；La doping；Mechanical properties；DBTT

摘要：Powder metallurgy methods were utilized to prepare lanthanum-doped titanium-zirconium-molybdenum (La-TZM) and traditional TZM alloy plates. Tensile and Charpy impact tests were employed to study the room temperature and cryogenic mechanical properties of the two kinds of TZM alloys. For the same process conditions, the lanthanum doping has significantly improved the tensile strength and elongation, which increased by 28.2% and 32.8%, respectively. For these process conditions, the La-TZM has higher density and smaller evenly distributed secondary phases. Compared with TZM, the secondary phase in La-TZM is finer, and hinders the spreading of cracks. This is why the La-TZM alloy plates have higher strength and elongation. By doping lanthanum, the ductile-to-brittle transition temperature of the TZM alloy decreased from -80 °C to -120 °C. The secondary phase La particles refine the grain and hinder fracture expansion across the grains during the impact fracture of the La-TZM alloy. TZM alloy improved room temperature and cryogenic mechanical properties significantly expand its application range.

备注：胡平

合写作者：AlexA.Volinsky,于志涛,谭江飞,宋瑞,胡卜亮,王华,何欢承

第一作者：王快社,杨帆,胡平

论文类型：期刊论文

卷号：卷：

期号：期：52

页面范围：页：131-136

是否译文：否

发表时间：2015-09-01