关键字：中文关键字：本体改性；聚偏氟乙烯；生活污水；膜生物反应器，英文关键字：Blending modification; Polyvinylidene Fluoride; Do

摘要：Ammonium persulphate (APS) was used as a novel additive for blending modification of Polyvinylidene Fluoride (PVDF) membrane in this study. The addition of APS changed the macroscopic and micro-structure of membrane, as the small scaly aggregates appeared and hydrophilicity increased slightly. Comparing with blank membrane, the specific surface area of PVDF membrane was reduced from 19.98 m2/g to 7.95 m2/g, and the total adsorption average pore size of membrane was increased from 89.82 nm to 253.58 nm when 0.7% of APS was added. During the short term filtration, the pure water flux of blank membrane was reduced by 61% and 81% after the first and second testing cycle, respectively. As a comparison, it was only reduced by 39% and 60% for 0.7% APS modified membrane. The effluent turbidity values of those modified membranes were all lower than that of blank membrane. During the long term operation in MBR, the filtration time of 0.7% APS modified membrane lasted for 21 days including 2 operational cycles. Comparing with modified membrane, the filtration time of blank membrane only lasted for 19 days, which included 3 times of membrane cleaning.

备注：刘嘉栋

合写作者：马亚斌,孟海龙

第一作者：王磊,于莉芳,高波,刘嘉栋

论文类型：期刊论文

卷号：卷：165

期号：期：

页面范围：页：78-85

是否译文：否

发表时间：2016-03-01