发表刊物:Materials Science Forum
关键字:中文关键字:冷拉;珠光体钢丝;球化退火,英文关键字:Severely cold drawing. Pearlitic steel wires; Sphe
摘要:The effects of spheroidizing annealing process on SWRH72B heavily cold drawn pearlite steel wires were studied and the mechanisms of low-temperature spheroidizing annealing were discussed. The results show that, with increasing drawing strain, the spheroidizing annealing temperature and time decreased and uniformity of the spheroidizing increased; the mechanism of low-temperature spheroidizing annealing was different from the traditional one of heavily cold drawn pearlite steel wires. When the true strains were between 2.85 and 5.1, the spheroidizing process of carbide could be divided into two stages: partial dissolution of lamellar carbide, and the precipitation and accumulation of compulsory dissolved cementite. When the true strains were larger than 5.1, the spheroidizing process of carbide was only characterized by precipitation and accumulation of compulsory dissolved cementite.
备注:刘世锋
第一作者:王伯健,刘世锋
论文类型:期刊论文
卷号:卷:682
期号:期:
页面范围:页:19-23
是否译文:否
发表时间:2011-01-01