关键字：中文关键字：混凝土；裂缝渗漏；高吸水性树脂，英文关键字：concrete; leakage through cracks; super-absorbent

摘要：Concrete leakage through cracks is a key factor resulting in the deterioration of concrete structures. This work presented a method to repair concrete leakage through cracks by treated with super-absorbent resin (SAR) synthesized in situ. The procedures of this method are to inject the precursor solution of polymer(acrylic acid-co-acrylamide) with initiator and crosslinker into concrete cracks, then use infrared ray to radiate and make the precursor solution copolymerize in situ. The synthesized SAR can absorb water and swell, thus filling cracks and preventing leakage of concrete. The impermeability of concrete coring with through cracks repaired by synthesizing SAR in situ was tested before and after being subjected to the attacks of acid, alkali, salts, dry-wet cycles and ultraviolet aging. Meantime, the absorbency of SAR was also evaluated by measuring the changes of swelling ratio before and after being subjected to the attacks of the same deteriorating factors. The experimental results show that the equilibrium-swelling ratio of SAR can sharply decrease after the attacks of acid and salt, and the impermeability of concrete cracks repaired with SAR is mainly governed by the swelling ratio of SAR and the width of cracks.

备注：宋学锋

合写作者：weijunfa,Hetingshu

第一作者：宋学锋

论文类型：期刊论文

卷号：卷：23

期号：期：

页面范围：页：386-391

是否译文：否

发表时间：2009-01-01