Cathode Preparation of Electrochemical Reduction Process of TiO2 to Titanium
发布时间：2024-08-09
点击次数：
- 所属单位：
- 冶金工程学院
- 发表刊物：
- 稀有金属材料与工程
- 关键字：
- 中文关键字：二氧化钛;钛;电化学还原;电极;烧结，英文关键字：Titanium;titanium dioxide;electrochemical reductio
- 摘要：
- The process of electrochemical reduction of TiO2 to sponge titanium involves pressure molding the TiO2 powder, sintering the pressed pellets and subjecting the sintered pellets to electrolysis in CaCl2 molten salt, in which cathode preparation is one of the important steps. In this work, the sintering parameters of the pressed pellet such as the sintering temperature and time were investigated. The SEM and EDS methods were applied to study the influences of sintering temperature and time on microstructure and porosity of the TiO2 pellets; moreover, the influences of sintering technological parameters on the microstructure and oxygen content of the electrochemical reduction products were studied. Pellet with coarser grain size was obtained when sintered at higher temperature and for longer time; while the change of the porosity in a pellet was complex under different sintering conditions. The oxygen concentration of the electrochemical-reduced products depended on grain size and porosity of the sintered pellets in this study: pellets with small grains could be fully reduced; both open pores and closed pores in the pellets were favorable to electro-reduction process. The proper electrode preparation condition was sintering the pressed pellet in 1000-1100℃ for 4h according to the results of the experiments.
- 备注：
- 王碧侠
- 合写作者：
- 周廉,崔静涛
- 第一作者：
- 赵西成,兰新哲,王碧侠
- 论文类型：
- 期刊论文
- 卷号：
- 卷：39
- 期号：
- 期：9
- 页面范围：
- 页：1513-1518
- 是否译文：
- 否
- 发表时间：
- 2010-09-01
- 上一条：工业纯钛TA2熔盐电解法渗硼的渗层生长动力学
- 下一条：TC4钛合金熔盐电解法渗硼