所属单位：

冶金工程学院

发表刊物：

Trans Tech Publications

关键字：

中文关键字：钒；高强钢；耐延迟断裂；PC钢，英文关键字：Vanadium; High strength steel; Delayed Fracture Re

摘要：

The delayed fracture resistance of pre-stressed concrete (PC) steel bar with different vanadium contents was investigated by using tensile sustained load delayed fracture test and optical microscope. The experimental results show that delayed fracture resistance of vanadium containing steels is higher than that of conventional steel 30MnSi at the same strength level and it increases with the increase of vanadium content. The improvement is resulted mainly from the irreversible traps for hydrogen and the prior austenite grain size refinement by vanadium carbide particles.

备注：

肖桂枝

第一作者：

庞玉华,王庆娟,肖桂枝

论文类型：

期刊论文

卷号：

卷：634-638

期号：

期：

页面范围：

页：4

是否译文：

否

发表时间：

2012-12-01