Dissolution-precipitation mechanism of self-propagating high-temperature synthesis of TiC-Cu cermet
发布时间:2024-08-09
点击次数:
- 所属单位:
- 材料科学与工程学院
- 发表刊物:
- journal of university of science and technology beijing
- 关键字:
- 中文关键字:TiC-Cu金属陶瓷,自蔓延高温合成,显微结构演变,合成机理,燃烧波前沿淬熄法,英文关键字:TiC-Cu cermet, Self-propagating high-temperature s
- 摘要:
- A mechanism of self-propagating high-temperature synthesis (SHS) of TiC-Cu cermet was studied by means of a combustion front quenching method. Microstructural evolution in the quenched sample was observed using a scanning electron microscope (SEM) with energy dispersive X-ray (EDX) spectrometry, and the combustion temperature were measured. The results showed that the combustion reaction started with a local formation of a Ti-Cu liquid solution and could be described with a dissolution-precipitation mechanism, namely, Ti, Cu and C particles dissolved into the Ti-Cu solution and TiC particles precipitated in the saturated Ti-Cu-C liquid solution. The local formation of the Ti-Cu solution resulted from a solid diffusion between the Ti and Cu particles.
- 备注:
- 肖国庆
- 合写作者:
- FengDuan,GangZhang,QunchengFan
- 第一作者:
- 肖国庆
- 论文类型:
- 期刊论文
- 卷号:
- 卷:14
- 期号:
- 期:6
- 页面范围:
- 页:568-572
- 是否译文:
- 否
- 发表时间:
- 2007-12-01