所属单位：

化学与化工学院

发表刊物：

Advaced Materials Research

关键字：

中文关键字：高钒高速钢；球墨铸铁；轧辊；激光熔覆，英文关键字：High Vanadium High Speed Steel; Nodular Cast Iron;

摘要：

As withstanding very high loads, thermal cycling leading to thermal fatigue, and severe environmental in the steel industry, rolls with long service life are specially required. High speed steel with high vanadium content is a newly-developed wear-resistance material that has been studied and used in some countries for making steel rolls. As a surface treatment technology, laser cladding can fabricate coating to improve the wear resistance of substrate. In this paper, the substrates for laser cladding were nodular cast iron rolls, Nd: YAG solid pulsed laser and continuous wave diode laser were both used to explore the feasibility of preparation high vanadium high speed steel (HVHSS) coatings. The Nd: YAG laser cladding results that the coated layers combined metallurgically with the substrate with a lot of microcracks. The average microhardness up to 650 HV is more than 2 times as high as that of the substrate. After laser remelting, a fully dense and crack free HVHHS coating with an excellent metallurgical bonding was deposited. The presence of VC in the coating mainly improves the microhardness of coating up to about 650 HV.

备注：

许妮君

合写作者：

JianbinLv,TingSun,ChangshengLiu

第一作者：

许妮君

论文类型：

期刊论文

卷号：

卷：712-715

期号：

期：

页面范围：

页：611-614

是否译文：

否

发表时间：

2013-06-01