Bi1.5Y0.3Sm0.2O3-La0.8Sr0.2MnO3–δ dual-phase composite hollow fiber membrane for oxygen separation
发布时间：2024-08-09
点击次数：
- 所属单位：
- 材料科学与工程学院
- 发表刊物：
- Materials Letters
- 关键字：
- 中文关键字：陶瓷；中空纤维；氧渗透；电性能，英文关键字：Ceramic; Hollow fiber; Oxygen permeation; Electric
- 摘要：
- Dense Bi1.5Y0.3Sm0.2O3-La0.8Sr0.2MnO3–δ hollow fiber membrane was fabricated by the combined phase inversion/sintering technique. The hollow fiber possessed an asymmetric structure. The oxygen permeability of the hollow fiber was measured by exposing its shell side to ambient air and sweeping the core side with helium to carry away the permeated oxygen. An oxygen permeation flux 3.9×10–7 mol cm–2 s–1 was obtained at 850℃ under a gradient of air/helium. The oxygen permeation flux was related to the helium sweeping rate, the length of the hollow fiber and the oxygen partial pressure on the feed side, and can be further increased by modifying the membrane surfaces.
- 备注：
- 杨春利
- 第一作者：
- 许启明,杨春利
- 论文类型：
- 期刊论文
- 卷号：
- 卷：65
- 期号：
- 期：23-24
- 页面范围：
- 页：3365-3367
- 是否译文：
- 否
- 发表时间：
- 2011-12-01